This study evaluated the effect of artificially accelerated aging (AAA) on the surface hardness of eight composite resins: Filtek Z250, Filtek Supreme, 4 Seasons, Herculite, P60, Tetric Ceram, Charisma, and Filtek Z100. Sixteen specimens were made from the test piece of each material, using an 8.0 × 2.0 mm teflon matrix. After 24 hours, eight specimens from each material were submitted to three surface hardness readings using a Shimadzu Microhardness Tester for 5 seconds at a load of 50 gf. The other eight specimens remained in the artificially accelerated aging machine for 382 hours and were submitted to the same surface hardness analysis. The means of each test specimen were submitted to the Kolmogorov-Smirnov test (p > 0.05), ANOVA and Tukey test (p < 0.05). With regard to hardness (F = 86.74, p < 0.0001) the analysis showed significant differences among the resin composite brands. But aging did not influence the hardness of any of the resin composites (F = 0.39, p = 0.53). In this study, there was interaction between the resin composite brand and the aging factors (F = 4.51, p < 0.0002). It was concluded that notwithstanding the type of resin, AAA did not influence surface hardness. However, with regard to hardness there was a significant difference among the resin brands.

Neste trabalho, envolvendo polímeros biodegradáveis, buscou-se obter indicadores por meio da análise de patentes para avaliar as perspectivas e oportunidades de atuação da área de polímeros. Utilizou-se para tal a base de dados Espacenet e o software Vantage Point. São matéria desse estudo os polímeros: poli(hidroxibutirato) - PHB, poli(hidroxibutirato-co-hidroxivalerato) - PHBV, poli(ácido lático) - PLA, poli(épsilon-caprolactona) - PCL e os polihidroxialcanoatos (PHAs), tratados mais detalhadamente por serem a classe geral dos poliésteres microbiais. Verificou-se que a área de polímeros biodegradáveis, apesar de recente e em desenvolvimento, apresenta grande potencial mediante o panorama atual de consumo dos materiais poliméricos. Observou-se, de uma forma geral, uma grande diversidade de temas e oportunidades de estudo em compostos, blendas, biodegradação e aplicações.

This work on biodegradable polymers involved an analysis of patents to identify indicators for evaluating the prospects and opportunities of action in the field of polymers. We used the Spacenet database and Vantage Point software. The study encompassed the following polymers: polyhydroxybutyrate - PHB, polyhydroxybutyrate-co-hydroxyvalerate - PHBV, polylactic acid - PLA, poly (epsilon-caprolactone) - PCL and the polyhydroxyalkanoates (PHAs), dealt in greater detail because they represent the general class of microbial polyesters. We found that, although the field of biodegradable polymers is new and still under development, it holds great potential in view of present widespread use of polymeric materials. Overall we found a great diversity of themes and opportunities for studies on compounds, blends, biodegradation and applications.

No gerenciamento do resíduo sólido urbano (RSU), a reciclagem surge como uma das vias para reduzir os resíduos sólidos aterrados em solo. Os plásticos constituem uma das classes de materiais com menor índice de reciclagem. Neste trabalho, as principais dificuldades encontradas em diversos países para aumentar os índices de reciclagem dos plásticos e as propostas que estão sendo utilizadas para mudar este cenário foram apresentadas. Por último, também foi apresentado um panorama geral sobre as exigências e limitações do retorno do plástico reciclado para alimentos. Este segmento representa todo um nicho de mercado que pode agregar valor e, principalmente, aumentar os índices de reciclagem de modo sustentável desde que haja investimentos em tecnologias inovadoras e economicamente viáveis.

In the management of municipal solid waste (MSW), recycling emerges as one of the ways to reduce the solid wastes deposited in landfills. Plastics are one of the classes of materials with the lowest recycling index. The present study deals with the main difficulties encountered in different countries to increase plastics recycling and the procedures adopted to change this scenario. Additionally, the general requirements and the restrictions about the use of recycled plastic for food contact are presented. This application represents a whole market share to be explored, which could add value and increase the recycling indexes in a sustainable way, provided that investments in innovative technologies are made.

Na sociedade contemporânea, uma solução ou um equacionamento minimamente satisfatório para os graves problemas ambientais decorrentes da larga utilização de polímeros tem se constituído num dos grandes desafios colocados para a comunidade científica. Na busca por soluções desejáveis, e como alternativa aos polímeros convencionais, os polímeros biodegradáveis têm sido alçados a uma posição de destaque. Dessa maneira, as pesquisas em torno desses compostos também vão adquirindo fundamental importância. Nesse trabalho, apresentamos os resultados da avaliação da biodegradação do poli-beta-(hidroxibutirato) (PHB), o poli-beta-(hidroxibutirato-co-valerato) (PHB-V) e o poli-(épsilon-caprolactona) (PCL) em solo compostado, utilizando a técnica de biodegradação aeróbia conhecida como Teste de Sturm. As análises térmicas destes polímeros foram realizadas usando calorimetria exploratória diferencial (DSC) e a temperatura de fusão e a cristalinidade, para cada polímero, foram determinadas. Os resultados mostraram que o PHB degradou mais rápido que os dois outros polímeros, provavelmente por causa da sua estrutura química que pode ser atacada mais facilmente pelos microorganismos.

In contemporary society, a solution or a minimally satisfying approach to the serious environmental problems stemming from the widespread use of polymers has been one of the great challenges the scientific community has had to cope with. The studies around these compounds, including their biodegradability, have acquired fundamental importance. In this work, we present the results from an evaluation of the biodegradation of poly-beta-(hydroxybutyrate) (PHB), poly-beta-(hydroxybutyrate-co-valerate) (PHB-V) and poly-(epsilon-caprolactone) (PCL), with products obtained from composting of municipal solid wastes, using the technique of aerobic biodegradation characterization known as Sturm Test. The thermal analysis of these polymers was done using differential scanning calorimeter (DSC). The melting temperature and crystallinity were also determined. The biodegradation test showed that PHB degraded faster than the other two polymers, probably because the chemical structure of this polymer made the attack by microorganisms easier.

A degradação derivada do processamento, uso, descarte, lavagem e reprocessamento foram caracterizados neste estudo. Para o HDPE/PP pós-consumo, a degradação foi estudada em função da presença de garrafas de HDPE/LDPE reprocessadas (recicladas) e da presença de tampas e rótulos de LDPE e PP. Esses materiais mostraram uma influência significativa na degradação total de HDPE/PP apenas quando presentes em conjunto. Os resíduos que apresentaram menor estabilidade termo-oxidativa foram os rótulos e tampas de LDPE e PP. As análises usadas na caracterização da influência destes resíduos foram espectroscopia do Infra-vermelho (IR) e Calorimetria Diferencial Exploratória (tempo de indução oxidativa - OIT). Além disso, a degradação do PET foi estudada em função das condições de lavagem e da presença de resíduos de soda cáustica e adesivo. Foram usadas medidas de viscosidade intrínseca e de titulação para caracterizar estas variáveis. Foi observado que apesar do uso de altas temperaturas (80 ºC) durante a lavagem, a extensão de tempo desta etapa (5 ou 15 min) não afetou a degradação do PET, pelo menos não em níveis detectáveis pelas análises. No entanto, a remoção do resíduo de adesivo mostrou uma influência significativa na degradação catalítica do PET.

The degradation derived from processing, use, disposable, washing and reprocessing was characterized in this study. The post-consumer HDPE/PP degradation was studied as a function of the presence of reprocessed (recycled) HDPE/LDPE bottles and of the presence of labels and cap of LDPE and PP. Those materials only showed a significant influence in the total degradation of HDPE/PP when they were present together. The residues that exhibited lower thermal-oxidative stability were the labels and cap of LDPE and PP. The analysis used to characterize their influence were Infrared Spectroscopy (IR) and Differential Scanning Calorimetry (oxidation induction time - OIT). Furthermore, the degradation of recycled PET. Furthermore, the PET degradation was studied as a function of washing conditions and of the presence of washing caustic residue and label adhesive. Intrinsic viscosity and titration measurements was used to characterize PET degradation. In spite of the use of high temperature (80 ºC) in the washing step, the time extent of that step (5 or 15 min) has not affected PET degradation, at least not detectable by the analysis used to characterize. The removing of adhesive residue played a helpful role, inhibiting the catalytic degradation of PET.

Este artigo contém uma revisão sobre o Poli(etileno naftalato) - PEN e também inclui vários aspectos relacionados com as blendas poliméricas Poli(etileno tereftalato) - PET / Poli(etileno naftalato) - PEN. O artigo é resultado de um desenvolvimento conjunto da Alcoa Alumínio S.A.- Divisão de Embalagens e do Departamento de Engenharia de Materiais - Universidade Federal de São Carlos (UFSCar), que tem como objetivo pesquisar o tema aqui abordado.

This paper presents a review on poly(ethylene naphtalate) - PEN including several features related to poly(ethylene terephtalate) - PET / poly(ethylene naphtalate) - PEN blends.The paper is a result of a conjoint development of Alcoa S.A. - Packaging Divisions and of the Department of Materials Engineering - Federal University of São Carlos (UFSCar), whose scope is to investigate the subject here approached.

O Negro de fumo (NF) é muito utilizado como um aditivo fotoprotetor em polímeros termoplásticos, principalmente para o polietileno de baixa densidade (PEBD) e para o polipropileno (PP). O comportamento como estabilizante termooxidativo do negro de fumo modificado superficialmente foi estudado, completando sua caracterização como agente fotoestabilizante. A superfície do negro de fumo foi modificada através da oxidação com peróxido de hidrogênio e com ácido nítrico, a fim de aumentar o seu caráter ácido. Os resultados desta estabilização termooxidativa foram positivos para o PEBD, mas mostraram comportamento insatisfatório para o PP.

Carbon black (CB) is very used as photoprotective additive in thermoplastic polymers, particularly Low Density Polyethylene (LDPE) and Polypropylene (PP). The thermooxidative stabilization behavior of carbon black modified superficially was studied, complementing its characterization as photostabilizing agent. To increase the carbon black acid character, its surface has been modified by hydrogen peroxide and nitric acid oxidation. The result of this thermooxidative stabilization was positive for LDPE but it was negative for PP.